First Aluminimumun welds. Critics please
« on: March 11, 2010, 11:02:13 PM »
These are some of my first aluminum welds.  It is .025 aluminum so ubber thin which made it a bitch.  Probably why I had some much trouble with the T welds. 



Logged
Quote from: bigdaddyvtec on June 04, 2009, 02:12:56 AM
You hhave just failed on so many levels, im waiting for someone else to verbally slap you in the gooch with a mallet

dvst8r

  • Certified OG
  • *****
  • Offline Offline
  • Posts: 3737
  • Unobtainium
Re: First Aluminimumun welds. Critics please
« Reply #1 on: March 11, 2010, 11:07:13 PM »
You have a couple with decent consistency, looks like you have the right idea, just need to keep doing it.
Logged
There are two kinds of people: Sheep and sharks. Sharks are winners and they don'#039#039t look back '#039#039cause they don'#039#039t have necks. Necks are for sheep.

turbob16hatch

  • Certified OG
  • *****
  • Offline Offline
  • Posts: 2080
Re: First Aluminimumun welds. Critics please
« Reply #2 on: March 11, 2010, 11:10:46 PM »
How are you welding this are you pulsing or are you just dabbing?
Logged

malichite

  • Administrator
  • Certified OG
  • *****
  • Offline Offline
  • Posts: 1988
  • Harbor Freight Ninja!
Re: First Aluminimumun welds. Critics please
« Reply #3 on: March 11, 2010, 11:13:05 PM »
Just dabbing.  I tried the pulser once and that is the fucked up one in the middle at the bottom.  The rest are all just dabbing.
Logged
Quote from: bigdaddyvtec on June 04, 2009, 02:12:56 AM
You hhave just failed on so many levels, im waiting for someone else to verbally slap you in the gooch with a mallet

turbob16hatch

  • Certified OG
  • *****
  • Offline Offline
  • Posts: 2080
Re: First Aluminimumun welds. Critics please
« Reply #4 on: March 11, 2010, 11:23:52 PM »
What rod, amps, etc.... I almost always run hot on Aluminum as i hate running the risk of not having a good tie in.
Logged

dvst8r

  • Certified OG
  • *****
  • Offline Offline
  • Posts: 3737
  • Unobtainium
Re: First Aluminimumun welds. Critics please
« Reply #5 on: March 11, 2010, 11:27:19 PM »
Quote from: turbob16hatch on March 11, 2010, 11:23:52 PM
... I almost always run hot on Aluminum as i hate running the risk of not having a good tie in.

This. I pretty much always start Aluminum foot to the floor, and then just ease back a touch once it is flowing.
Logged
There are two kinds of people: Sheep and sharks. Sharks are winners and they don'#039#039t look back '#039#039cause they don'#039#039t have necks. Necks are for sheep.

malichite

  • Administrator
  • Certified OG
  • *****
  • Offline Offline
  • Posts: 1988
  • Harbor Freight Ninja!
Re: First Aluminimumun welds. Critics please
« Reply #6 on: March 11, 2010, 11:31:16 PM »
1/16th r4043, 3/32 thoriated, gas lense, 120 amps, hit about 75% pedal, then backed off a little when it started flowing.  Seems the longer I welded the more I needed to back off the pedal. 
Logged
Quote from: bigdaddyvtec on June 04, 2009, 02:12:56 AM
You hhave just failed on so many levels, im waiting for someone else to verbally slap you in the gooch with a mallet

dvst8r

  • Certified OG
  • *****
  • Offline Offline
  • Posts: 3737
  • Unobtainium
Re: First Aluminimumun welds. Critics please
« Reply #7 on: March 11, 2010, 11:35:05 PM »
Quote from: malichite on March 11, 2010, 11:31:16 PM
...Seems the longer I welded the more I needed to back off the pedal. 

That happens in small work pieces as they heat up, you need less heat input. 
Logged
There are two kinds of people: Sheep and sharks. Sharks are winners and they don'#039#039t look back '#039#039cause they don'#039#039t have necks. Necks are for sheep.

Teg2boo

  • Certified OG
  • *****
  • Offline Offline
  • Posts: 4261
Re: First Aluminimumun welds. Critics please
« Reply #8 on: March 11, 2010, 11:51:22 PM »
Quote from: n/a michael on March 11, 2010, 11:05:59 PM
looks a shit load better than buk's welding  :-*

Yeah, where are the holes? You're doing it wrong man! :P
Logged


damn you guys too? its a fucking forum not a court room!
 Its not a forum its a gang.  

onlyflash944

  • Certified OG
  • *****
  • Offline Offline
  • Posts: 2741
  • Jack of all trades, Master of none
Re: First Aluminimumun welds. Critics please
« Reply #9 on: March 12, 2010, 12:55:49 AM »
Quote from: n/a michael on March 11, 2010, 11:05:59 PM
looks a shit load better than buk's welding  :-*

i've had bowel movements that looked better than buks welding
Logged

You read some forums? nbspnbsp Cool, I tune cars.

  Its your fucking car, if you want to hack it up fucking go for it.

turbob16hatch

  • Certified OG
  • *****
  • Offline Offline
  • Posts: 2080
Re: First Aluminimumun welds. Critics please
« Reply #10 on: March 12, 2010, 12:37:18 PM »
Quote from: onlyflash944 on March 12, 2010, 12:55:49 AM
Quote from: n/a michael on March 11, 2010, 11:05:59 PM
looks a shit load better than buk's welding  :-*

i've had bowel movements that looked better than buks welding

haha
Logged

jundoc

  • Sr. Member
  • ****
  • Offline Offline
  • Posts: 671
Re: First Aluminimumun welds. Critics please
« Reply #11 on: March 12, 2010, 10:16:31 PM »
looking good....
Logged