Author Topic: i think i maybe worse than buk  (Read 5860 times)

2slow

  • Sr. Member
  • ****
  • Offline Offline
  • Posts: 539
i think i maybe worse than buk
« on: April 26, 2010, 04:14:28 PM »
so i can lay a bead fine just running over some stock but when it comes to joining two piece of metal i suck ass. this is a walmart welder with hf 6011 rods. it got the job done but i had to weld like ten thousand patches to fill holes in the thin ass down pipe metal

this is going on my d15b7 92 dx 4dr

btw the basketball got kicked under the car when i was mowing the lawn
« Last Edit: April 26, 2010, 04:16:29 PM by 2slow »
Logged

Teg2boo

  • Certified OG
  • *****
  • Offline Offline
  • Posts: 4261
Re: i think i maybe worse than buk
« Reply #1 on: April 26, 2010, 04:29:54 PM »
Looks good.
Logged


damn you guys too? its a fucking forum not a court room!
 Its not a forum its a gang.  

patsmx5

  • Certified OG
  • *****
  • Offline Offline
  • Posts: 1584
Re: i think i maybe worse than buk
« Reply #2 on: April 26, 2010, 04:36:34 PM »
Logged
Quote: Originally Posted by Adam Hopkins
There is no such thing as too much boost. You could have too little rod, piston, or sleeve. But never too much boost.

Minor Threat

  • Certified OG
  • *****
  • Offline Offline
  • Posts: 2401
Re: i think i maybe worse than buk
« Reply #3 on: April 26, 2010, 05:14:06 PM »
Why the fuck are you using those rods?
Logged
"quotquotand the welds look like a pigeon had 1 too many chili-dogs, whoever built them needs to go throw their tools in the ocean."quotquot

www.facebook.com/enhancedautoperformance

bigwig

  • Guest
Re: i think i maybe worse than buk
« Reply #4 on: April 26, 2010, 05:21:37 PM »
Do yourself a favor and go get a HF $120 mig welder.  Then go to the local welding supply store and get some name brand fluxcore wire.  Stick welding 16 gauge material is not easy.
Logged

t_cel_t

  • Certified OG
  • *****
  • Offline Offline
  • Posts: 3147
Re: i think i maybe worse than buk
« Reply #5 on: April 26, 2010, 05:25:26 PM »
god damn what is wrong with you guys, always trying to weld the rustiest metal together. your welds would go so much easier if you just took a fucking wire brush to the metal for like 30 sec.
Logged
malone labe

I think all cop cars need to have turbo. nbspnbsp Then they would understand the necessity of putting your foot down and how uncontrollable the urge is to fucking rail on that shit.

SgtB

  • Sr. Member
  • ****
  • Offline Offline
  • Posts: 406
Re: i think i maybe worse than buk
« Reply #6 on: April 26, 2010, 06:15:16 PM »
80% prep, 20% welding.
Logged

t_cel_t

  • Certified OG
  • *****
  • Offline Offline
  • Posts: 3147
Re: i think i maybe worse than buk
« Reply #7 on: April 26, 2010, 07:34:48 PM »
Quote from: SgtB on April 26, 2010, 06:15:16 PM
80% prep, 20% welding.
iron oxide(rust) is non-conductive
Logged
malone labe

I think all cop cars need to have turbo. nbspnbsp Then they would understand the necessity of putting your foot down and how uncontrollable the urge is to fucking rail on that shit.

2slow

  • Sr. Member
  • ****
  • Offline Offline
  • Posts: 539
Re: i think i maybe worse than buk
« Reply #8 on: April 26, 2010, 08:51:35 PM »
Quote from: Minor Threat on April 26, 2010, 05:14:06 PM
Why the fuck are you using those rods?
becuase i dont know what kind of metal i was welding and was under the impression that 6011 was kind of a general purpose multi metal welding rod
Quote from: t_cel_t on April 26, 2010, 05:25:26 PM
god damn what is wrong with you guys, always trying to weld the rustiest metal together. your welds would go so much easier if you just took a fucking wire brush to the metal for like 30 sec.
the flange rusted after i welded. i used my welding hammer/brush every time i started a new weld
Logged

HiProfile

  • Certified OG
  • *****
  • Offline Offline
  • Posts: 4564
  • Injector Kingpin
Re: i think i maybe worse than buk
« Reply #9 on: April 26, 2010, 11:34:34 PM »
Quote from: 2slow on April 26, 2010, 04:14:28 PM
i think i maybe worse than buk

Well at least your two pieces seem to be fused together. Buk just burns holes in shit.

And lol at basketball jackstand. C is for Safety!
Logged
they mspainted dildoes in my mom'#039#039s hand, in a picture of her in a hospital bed. -JD
dem gurls need some boobz! -Engloid

2slow

  • Sr. Member
  • ****
  • Offline Offline
  • Posts: 539
Re: i think i maybe worse than buk
« Reply #10 on: April 26, 2010, 11:55:27 PM »
Quote from: HiProfile on April 26, 2010, 11:34:34 PM
Quote from: 2slow on April 26, 2010, 04:14:28 PM
i think i maybe worse than buk

Well at least your two pieces seem to be fused together. Buk just burns holes in shit.

And lol at basketball jackstand. C is for Safety!
yeah i burnt a shit ton of holes in the thin ass chrome shit steel but i pathed it with pieces of autozone crush bend steel.
and about the basket ball also believe in saftey first, but then team work
Logged

PhilStubbs

  • Certified OG
  • *****
  • Offline Offline
  • Posts: 5885
  • Teh Secksy.....I has it
Re: i think i maybe worse than buk
« Reply #11 on: April 27, 2010, 08:24:45 PM »
im not sure whats worse, the basketball jackstand or the chords showing through that tire all the way around.
Logged
obd1>gtgtall

 fucking box started smoking and i saw a flame start up so i grabbed a bucket of water and splashed it on the breaker box.

2slow

  • Sr. Member
  • ****
  • Offline Offline
  • Posts: 539
Re: i think i maybe worse than buk
« Reply #12 on: April 28, 2010, 02:37:30 AM »
Quote from: SecksyPeePee on April 27, 2010, 08:24:45 PM
im not sure whats worse, the basketball jackstand or the chords showing through that tire all the way around.
in all seriouness the basketball was kicked under there when mowing the lawn. the reason why the jackstand was not under it is becuase i had them on the fron lower rad support and it got in the way of putting the bumper back on there is a jack under the car on the driverside seam. and yes those tires are fucked they were put on to moved the car is all and have since been replaced. ill start a build thread on this pos when its done or almost done
Logged

onlyflash944

  • Certified OG
  • *****
  • Offline Offline
  • Posts: 2741
  • Jack of all trades, Master of none
Re: i think i maybe worse than buk
« Reply #13 on: April 29, 2010, 06:33:09 PM »
find the smallest 6013 rods you can.  they fill holes better, and the smaller the diameter the lower amps you can run which leads to less holes. 


shit looks aweful.  good work
Logged